Stat-Rite® M2809
| Category: | Acrylic, Unspecified , Acrylic |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Stat-Rite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QvlEx8_Stat-Rite-M2809.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stat-Rite® M2809 is a static dissipative acrylic alloy. Stat-Rite® M2809 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to provide clean, permanent ESD protection. Stat-Rite® IDP alloys provide consistent static dissipation even when injection molded into components. FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 26.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 1450 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 75.0 | °C | |
| 1.8 MPa, Unannealed | 67.2 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+10 | ohms·cm | ASTM D257 |
| Static Decay - 1000 V to 10V, 50% R.H. | < 1.0 | sec | CPM |
| Surface Resistance - 12% R.H. | 6.0E+9 | ohms | ESD S11.11 |
| Surface Resistivity - 50% R.H. | 1.0E+10 | ohms/sq | ASTM D257 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | IDP Alloy | ||
| Ionic Content | Internal Method | ||
| Cation Na | 200 | ng/cm² | |
| Cl Anion 1 | 20.0 | ng/cm² | |
| NO3 Anion 2 | 5.00 | ng/cm² | |
| PO4 Anion 3 | 15.0 | ng/cm² | |
| SO4 Anion 4 | 20.0 | ng/cm² | |
| Outgassing 5 | Internal Method | ||
| MMA | 40.0 | µg/g | |
| Styrene | 15.0 | µg/g | |
| Toluene | 180 | µg/g | |
| Total Organics | 250 | µg/g |
| Note Message | |
|---|---|
| 1 . | Test Method #3010-4 |
| 2 . | Test Method #3010-4 |
| 3 . | Test Method #3010-4 |
| 4 . | Test Method #3010-4 |
| 5 . | Test Method #3010-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ II230 | Polymics, Ltd. | PEI | Pyramid™ |
| Talcoprene® 540TC NAT | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| Chemraz 543 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Hostacom EKC 430N | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ LUBRICOMP™ Cycoloy_C2801 compound | SABIC Innovative Plastics | PC+ABS | LNP™ LUBRICOMP™ |