Order Products : sales@su-jiao.com
Petrotene® PP A3 G50 HS PRTA010 PH384
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QvOAmh_Petrotene-PP-A3-G50-HS-PRTA010-PH384.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene in black colour reinforced with 50% glass fiber, heat stabilized, ideal for injection molding, good set of mechanical properties and dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 to 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 to 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.90 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.0 to 2.0 | % | ASTM D570 |
| Ash Content | 48 to 52 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9200 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 105 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 8750 | MPa | ASTM D790 |
| Flexural Strength | 155 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 15 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 160 | °C | ASTM D648 |
| Vicat Softening Temperature | 155 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HP132 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| Retpol® 9028 | PolyPacific Pty. Ltd. | PP Homopolymer | Retpol® |
| Gallonprene® GP520-5516 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Hytrel® PC966 NC010 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| PLANAC BT-2330 | TOYOBO America, Inc. | PBT | PLANAC |