POLYLAC® PA-709S
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QuLquo_POLYLAC-PA-709S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYLAC® PA-709S is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.03 | g/cm³ | ASTM D792 |
| 23°C | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 0.40 | g/10 min | |
| 220°C/10.0 kg | 4.5 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 75.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 36.0 | MPa | ISO 527-2/50 |
| Break | 28.0 | MPa | ISO 527-2/50 |
| 3.00 mm 1 | 36.3 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break, 3.00 mm 2 | 40 | % | ASTM D638 |
| Break | 30 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 6.00 mm 3 | 1960 | MPa | ASTM D790 |
| -- 4 | 1500 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.00 mm 5 | 54.9 | MPa | ASTM D790 |
| -- 6 | 51.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 33 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C, 3.00 mm | 430 | J/m | ASTM D256 |
| 23°C, 6.00 mm | 360 | J/m | ASTM D256 |
| -- | 31 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 86.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 95.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ASTM D1525 7 |
| -- | 104 | °C | ISO 306/A50 |
| -- | 98.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 190 to 210 | °C | |
| Cylinder Zone 3 Temp. | 210 to 240 | °C | |
| Cylinder Zone 5 Temp. | 220 to 250 | °C | |
| Die Temperature | 200 to 250 | °C |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp DBS3602 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Starflam AFR430B1 | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| Isocor™ 6100 | Shakespeare Monofilaments and Specialty Polymers | Nylon 610 | Isocor™ |
| LNP™ LUBRICOMP™ RKN14 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| TECACOMP® PEEK 450 ELS nano black 4134 | Ensinger GmbH | PEEK | TECACOMP® |