SCHULADUR® A GB 20
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULADUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qtgxhl_SCHULADUR-A-GB-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% glass bead reinforced PBT-grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 50.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 3300 | MPa | ISO 178 |
| Flexural Stress 2 | 83.0 | MPa | ISO 178 |
| Flexural Strain at Break | 8.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.5 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 30 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 175 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 94.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 218 | °C | ISO 306/A50 |
| -- | 184 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | 23 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.60 mm | HB | IEC 60695-11-10, -20 | |
| 3.20 mm | HB | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 725 | °C | IEC 60695-2-12 |
| 3.00 mm | 725 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 750 | °C | IEC 60695-2-13 |
| 3.00 mm | 750 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAZMID B 153 SP20 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 6 | MAZMID B |
| NaturePlast NP EL 009 | NaturePlast | TPE | NaturePlast |
| Nypol® PA A3 V30 HL PRTA010 NR366 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Sinvicomp SFC8017 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | SINVICOMP |
| Sylvin 9604-80 Clear Black 2106 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |