LNP™ LUBRICOMP™ LX92134 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qsi7kk_LNP-LUBRICOMP-LX92134-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* LX92134 is a compound based on Polyetheretherketone resin containing proprietary fillers. Added features of this material include: High Temperature Bearing Grade, Internally lubricated. Also known as: LNP* LUBRICOMP* Compound PDX-L-92134 Product reorder name: LX92134 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.0 to 1.4 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 73.0 | MPa | |
| Break | 72.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 4.7 | % | |
| Break | 6.8 | % | |
| Flexural Modulus 1 | 3600 | MPa | ISO 178 |
| Flexural Stress | 118 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.37 | ASTM D3702 Modified | |
| Flexural Strain at Break 2 | 6.3 | % | ISO 178 |
| Wear Factor - Washer | 41.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 201 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 152 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 5.1E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 6.0E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 to 360 | °C | |
| Middle Temperature | 366 to 377 | °C | |
| Front Temperature | 382 to 393 | °C | |
| Processing (Melt) Temp | 382 to 388 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CALP 3400GE | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Cheng Yu NG1300S | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| Kumho PPG 3602 | Korea Kumho Petrochemical Co., Ltd. | POP | Kumho PPG |
| LNP™ VERTON™ MV006SU compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |
| OxyVinyls® 216 | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |