LNP™ LUBRILOY™ D2000I compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QsZ3oA_LNP-LUBRILOY-D2000I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY D2000I is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, High Impact. Also known as: LNP* LUBRILOY* Compound D-HI Product reorder name: D2000I |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 49.6 | MPa | |
| Break | 54.5 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.6 | % | |
| Break | 130 | % | |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.32 | ||
| vs. Itself - Static | 0.22 | ||
| Wear Factor - Washer | 35.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 540 | J/m | ASTM D256 |
| 23°C | 780 | J/m | ASTM D256 |
| -40°C 1 | 43 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 120 | °C | ASTM D648 |
| CLTE | |||
| Flow : -40 to 40°C | 1.3E-4 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.4E-4 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 299 to 310 | °C | |
| Front Temperature | 304 to 316 | °C | |
| Processing (Melt) Temp | 304 to 316 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF9721 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Generic Nylon, Unspecified - Glass Fiber | Generic | Nylon, Unspecified | Generic |
| PENTAMID A SK H natur | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| Sylvin 5150-90 White 1324 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 2804-80 White 1440 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |