Kingfa PBT JE2-R2G30
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qs1UV4_Kingfa-PBT-JE2-R2G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PBT JE2-R2G30 is an acrylonitrile butadiene styrene PBT (ABS PBT) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa PBT JE2-R2G30 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 0.20 - 0.30 | % | ASTM D955 |
| Transverse flow : 23°C | 0.50 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 84 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 112 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus 3 | 9500 | MPa | ASTM D790 |
| Flexural Strength 4 | 185 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 130 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 118 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.30 mm | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 245 - 265 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 235 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 60.0 - 110 | °C | |
| Back Pressure | 0.300 - 1.00 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 265°CInjection Speed: 60 to 80% |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PPO SE1X701 | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| 3M™ Dyneon™ Fluoroplastic THV 500GX4Z | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroplastic |
| Evoprene™ GC 5689 | AlphaGary | SEBS | Evoprene™ GC |
| Exelene® LLDPE 20400 | Montachem International, Inc. | LLDPE | Exelene® LLDPE |
| Edgetek™ PK-30GF/000 EM BK | PolyOne Corporation | PEEK | Edgetek™ |