Fortron® CES50
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QrcbMh_Fortron-CES50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron CES50 is a 40% glass fiber reinforced material with a total chlorine content less than or equal to 900 ppm. It offers excellent physical properties similar to those of the Fortron 1140L6 product. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 170 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 13300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 51 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 44 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 262 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.200 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Feed Temperature: 60 to 80°CZone 4 Temperature: 330 to 340°CManifold Temperature: 330 to 340°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Surlyn® 9950 | DuPont Packaging & Industrial Polymers | EMAA | Surlyn® |
| Vexel 3250 | Custom Resins Group | PBT | Vexel |
| Vital-Line SHE5240B | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| ESTOPLAST ZK 6400WW31 | Ester Industries Ltd. | PC | ESTOPLAST ZK |
| PENTAMID B S GV50 H black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |