IROGRAN® A 87 H 4615
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QrYQ54_IROGRAN-A-87-H-4615.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 87 H 4615 is a thermoplastic polyester-polyurethane for injection moulding applications. Additional characteristics of the product are very short cycle times and high dimensional stability. PERFORMANCE FEATURES
APPLICATIONS For the production of mining screens, coupling halfs, technical parts, cylinders, buffers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.20 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 50.0 | cm³/10min | |
| Molding Shrinkage | |||
| Flow : Injection Molded | 0.80 | % | ASTM D955 |
| -- 2 | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A, Injection Molded | 80 | ASTM D2240 | |
| Shore D, Injection Molded | 30 | ASTM D2240 | |
| Shore A, Injection Molded | 85 | ISO 868 | |
| Shore D, Injection Molded | 35 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 3 | 25 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 4 | |||
| 100% Strain | 4.48 | MPa | ASTM D412 |
| 100% Strain | 6.00 | MPa | DIN 53504 |
| 300% Strain | 10.6 | MPa | ASTM D412 |
| 300% Strain | 14.0 | MPa | DIN 53504 |
| Tensile Strength 5 | |||
| Break | 38.6 | MPa | ASTM D412 |
| Break | 45.0 | MPa | DIN 53504 |
| Tensile Elongation 6 | |||
| Break | 650 | % | ASTM D412 |
| Break | 640 | % | DIN 53504 |
| Tear Strength 7 | |||
| -- | 89.3 | kN/m | ASTM D624 |
| -- | 80 | kN/m | ISO 34-1 |
| Compression Set 8 | |||
| 23°C, 24 hr | 25 | % | ASTM D395, ISO 815 |
| 70°C, 24 hr | 38 | % | ASTM D395 |
| 70°C, 24 hr | 40 | % | ISO 815 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Rear Temperature | 175 to 195 | °C | |
| Middle Temperature | 175 to 195 | °C | |
| Front Temperature | 175 to 195 | °C | |
| Nozzle Temperature | 180 to 200 | °C | |
| Processing (Melt) Temp | 170 to 195 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 165 to 190 | °C | |
| Cylinder Zone 2 Temp. | 165 to 190 | °C | |
| Cylinder Zone 3 Temp. | 165 to 190 | °C | |
| Cylinder Zone 4 Temp. | 165 to 190 | °C | |
| Cylinder Zone 5 Temp. | 165 to 190 | °C | |
| Adapter Temperature | 175 to 195 | °C | |
| Die Temperature | 175 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |
| 8 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® T080EY | Reliance Industries Limited | PP, HMS | REPOL® |
| Nanjing Hongrui PP P840 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| BCC Resins BC 5003 | BCC Products Inc. | Epoxy | BCC Resins |
| Complet® LGF40-PEI | PlastiComp, Inc. | PEI | Complet® |
| Laprene® 830000542 | SO.F.TER. SPA | SEBS | Laprene® |