NORYL™ WCA871A resin
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QrWOeP_NORYL-WCA871A-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant performance and mechanical properties capable of meeting UL VW-1 requirement and 105C temperature rating as defined UL1581. UL1581 tests conducted on 1.0mmD wire with AWG28 conductor. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 30 sec) | 87 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break | 30.0 | MPa | UL 1581 |
| Break 1 | 18.0 | MPa | ASTM D638 |
| Break, 136°C 2 | 27.0 | MPa | UL 1581 |
| Break | 18.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break | 280 | % | UL 1581 |
| Break 3 | 140 | % | ASTM D638 |
| Break, 136°C 4 | 200 | % | UL 1581 |
| Break | 130 | % | ISO 527-2/50 |
| Flexural Modulus 5 | |||
| 100 mm Span | 100 | MPa | ASTM D790 |
| -- | 100 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -40.0 | °C | ASTM D746 |
| UL Temperature Rating | 105 | °C | UL 1581 |
| Heat Deformation (121°C) 6 | 20 | % | UL 1581 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Smoke Density | ASTM E662 | ||
| Flame, 0.5 mm plaque, Ds, max | 140 | ||
| Non-Flame, 0.5 mm plaque, Ds, max | 67 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.4E+16 | ohms·cm | ASTM D257 |
| Electric Strength (1.50 mm, in Oil) | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.60 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 2.8E-3 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 825 | °C | IEC 60695-2-13 |
| Oxygen Index | 28 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | After 7 days |
| 3 . | Type I, 50 mm/min |
| 4 . | After 7 days |
| 5 . | 13 mm/min |
| 6 . | 250 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Queo™ 0203 | Borealis AG | Plastomer | Queo™ |
| SCHULADUR® A3 GF30 | A. Schulman Inc. | PBT+ASA | SCHULADUR® |
| Akulon® K224-G6-FC NA99001 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Cheng Yu ML3435 | Cheng Yu Plastic Company Limited | PC | Cheng Yu |
| HOPELEN FO-135 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |