Sup-tech H703
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qpf9dq_Sup-tech-H703.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech H703 is a Polyamide 46 (Nylon 46) product filled with 15% glass fiber. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | DIN 53479 |
| Molding Shrinkage | 5.0E-3 to 0.011 | % | DIN 53464 |
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 1.8 | % | |
| Saturation, 23°C | 3.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 135 | MPa | DIN 53455 |
| Tensile Strain (Break) | 3.0 | % | DIN 53452 |
| Flexural Modulus | 7300 | MPa | DIN 53457 |
| Flexural Stress | 210 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.5 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 270 | °C | |
| 1.8 MPa, Unannealed | 220 | °C | |
| Melting Temperature | 295 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Electric Strength | 24 | kV/mm | DIN 53481 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 9.0 to 18 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex SD-0170 F | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Ultraform® H 4320 PRO | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| AEI SX539 | AEI Compounds Limited | XLPE | AEI |
| Andur 9200 AP | Anderson Development Company | PUR-Ether/TDI | Andur |
| Fiberfil® J-60/GB/20 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |