Terralene® WF 6534
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Terralene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QoGbsl_Terralene-WF-6534.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High desnity polyethylene with narrow molar mass distribution, containing a medium amount of wood fibers and functional additives. Recommended for the production of injection moulded articles. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 to 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 26.0 | MPa | |
| Break | 25.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.0 | % | |
| Break | 4.5 | % | |
| Flexural Modulus | 2620 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 34.0 | MPa | ISO 178 |
| Flexural Strain at Break | 7 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 8.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 130 to 145 | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Measured on injection moulded specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vamac® GXF | DuPont Performance Elastomers | AEM | Vamac® |
| EZPrene 9040A | ENPLAST Americas, a Ravago Group Company | TPV | EZPrene |
| Felix Compounds Mica | Felix Compounds | PP+PE | Felix Compounds |
| EpoxAmite® 101 FAST | Smooth-On, Inc | Epoxy | EpoxAmite® |
| Kuraray Poval® PVA L-9 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |