KumhoSunny PBT/ASA HBA5830G
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PBT/ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qo8gQZ_KumhoSunny-PBT-ASA-HBA5830G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HBA5830G is a 30% glass reinforced PBT/ASA blend with excellent mechanical properties, high dimensional stability and low density. Applications: connectors and automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.45 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.30 to 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8000 | MPa | ISO 178 |
| Flexural Stress 2 | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed) | 190 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 235 to 240 | °C | |
| Middle Temperature | 240 to 260 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Processing (Melt) Temp | 245 to 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.200 to 0.800 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STYRON™ 486M | Trinseo | PS (HIPS) | STYRON™ |
| TOTAL Polypropylene PPH 4070 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Electrafil® ABS SS16 FR BK | Techmer Engineered Solutions | ABS | Electrafil® |
| LNP™ THERMOCOMP™ 2X95787 compound | SABIC Innovative Plastics | ETFE | LNP™ THERMOCOMP™ |
| Lucky Enpla LAY1001F SG | Lucky Enpla Co LTD | PC+ABS | Lucky Enpla |