OP - PPO PPOX-30GF
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QnS1VT_OP---PPO-PPOX-30GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OP-PPO PPOX-30GF is a polyphenylene ether + PS (PPE + PS) material, and its filler is 30% glass fiber reinforced material. This product is available in North America and is processed by injection molding. The main characteristics of OP-PPO PPOX-30GF are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (315°C/5.0 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.10 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 103 | MPa | ASTM D638 |
| Fracture | 103 | MPa | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 149 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 143 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | UL 94 | |
| 3.18 mm | HB | UL 94 |
| Additional Information |
|---|
| Melt Mass -Flow Rate (MFR), ASTM D1238, 315°C/ 5.0kg: 1 to 4 g/10 min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 260 - 304 | °C | |
| Middle Temperature | 271 - 310 | °C | |
| Front Temperature | 282 - 316 | °C | |
| Processing (Melt) Temp | 293 - 316 | °C | |
| Mold Temperature | 82.2 - 116 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8686-70 Clear 8365 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Axiall PVC 6511 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Fluon® LM-ETFE 730AP | Asahi Glass Co., Ltd. | ETFE | Fluon® |
| Hostacom EKC 330N E1 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Delene 1110 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |