LNP™ THERMOCOMP™ TF002 compound
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QmKIW9_LNP-THERMOCOMP-TF002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP TF002 is a compound based on Polyurethane resin containing 10% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound TF-1002 Product reorder name: TF002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.80 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.40 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.61 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1460 | MPa | ASTM D638 |
| -- | 1270 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 42.0 | MPa | ASTM D638 |
| Yield | 43.0 | MPa | ISO 527-2/5 |
| Break 3 | 38.0 | MPa | ASTM D638 |
| Break | 40.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 33 | % | ASTM D638 |
| Yield | 34 | % | ISO 527-2/5 |
| Break 5 | 53 | % | ASTM D638 |
| Break | 55 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 908 | MPa | ASTM D790 |
| -- 7 | 958 | MPa | ISO 178 |
| Flexural Stress | 26.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 330 | J/m | ASTM D256 |
| 23°C 8 | 31 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 9 | 130 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 29.0 | J | ASTM D3763 |
| -- | 24.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 152 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 148 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 67.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 61.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.7E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.0 to 104 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 193 to 210 | °C | |
| Middle Temperature | 193 to 216 | °C | |
| Front Temperature | 199 to 221 | °C | |
| Nozzle Temperature | 204 to 227 | °C | |
| Processing (Melt) Temp | 210 | °C | |
| Mold Temperature | 16.0 to 43.0 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROFIL™ PPH3GF17-BK | Pier One Polymers, Inc. | PP Homopolymer | PROFIL™ |
| RenPIM® VG 5281 Polyol/ 5281 Isocyanate | Huntsman Advanced Materials | PUR, Unspecified | RenPIM® |
| RTP VLF 81309 | RTP Company | PPS | RTP |
| SABIC® PP 510A | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| Elastollan® 560 D | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |