POCAN® KU 2-7604 000000

Category:	PC+PBT , Polycarbonate + PBT
Manufacturer:	LANXESS Corporation
Trademark:	POCAN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Qm7w3H_POCANKU27604000000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PBT+PC, non-reinforced, injection molding, extrusion, flame retardant, improved impact strength, low tendency to warp

General Information
Additive	Flame retardancy
Features	Low warpage Impact resistance, good Flame retardancy
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Extrusion Injection molding
Resin ID (ISO 1043)	(PBT+PC) FR (17)

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.30	g/cm³	ISO 1183
Apparent Density	0.80	g/cm³	ISO 60
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)	20.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 2577
Vertical flow direction : 250°C, 2.00mm ¹	0.80	%	ISO 2577
Vertical flow direction : 120°C, 4 hours, 2.00mm ²	0.80	%	ISO 2577
Flow direction : 250°C, 2.00mm ³	0.80	%	ISO 2577
Flow direction : 120°C, 4 hours, 2.00mm ⁴	0.80	%	ISO 2577
Water Absorption			ISO 62
Saturated, 23°C	0.30	%	ISO 62
Equilibrium, 23°C, 50% RH	0.10	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	93.0	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2000	MPa	ISO 527-2/1
Tensile Stress (Yield, 23°C)	45.0	MPa	ISO 527-2/50
Tensile Strain (Yield, 23°C)	3.5	%	ISO 527-2/50
Nominal Tensile Strain at Break (23°C)	> 20	%	ISO 527-2/50
Flexural Modulus ⁵(23°C)	2000	MPa	ISO 178/A
Flexural Stress			ISO 178/A
3.5% strain, 23°C	65.0	MPa	ISO 178/A
23°C ⁶	70.0	MPa	ISO 178/A
Flexural Strain at Flexural Strength ⁷(23°C)	5.0	%	ISO 178/A

Additional Information	Nominal Value		Test Method
ISO Shortname	PBT+PC, GFHLMPR, 11-020		ISO 7792

Injection	Nominal Value	Unit	Test Method
Residual Moisture Content	0.0 - 0.020	%	Karl Fisher

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	15	kJ/m²	ISO 179/1eA
23°C	60	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	No Break		ISO 179/1eU
23°C	No Break		ISO 179/1eU
Notched Izod Impact			ISO 180/1A
-30°C	15	kJ/m²	ISO 180/1A
23°C	50	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength			ISO 180/1U
-30°C	No Break		ISO 180/1U
23°C	No Break		ISO 180/1U

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	100	°C	ISO 75-2/B
1.8 MPa, not annealed	75.0	°C	ISO 75-2/A
Vicat Softening Temperature	115	°C	ISO 306/B120
Melting Temperature ⁸	225	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : 23 to 55°C	1.0E-4	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	1.1E-4	cm/cm/°C	ISO 11359-2

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (0.800 mm)	V-0		UL 94
Glow Wire Flammability Index (0.800 mm)	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature			IEC 60695-2-13
0.800 mm	775	°C	IEC 60695-2-13
1.60 mm	775	°C	IEC 60695-2-13
3.00 mm	775	°C	IEC 60695-2-13

Injection	Nominal Value	Unit	Test Method
Drying Temperature - Circulation Dryer	120	°C
Drying Time - Circulation Dryer	4.0 - 8.0	hr
Processing (Melt) Temp	240 - 260	°C
Mold Temperature	80.0 - 100	°C

Note Message
1 .	60x60x2mm, 80°C MT, 600 bar
2 .	60x60x2mm
3 .	60x60x2mm, 80°C MT, 600 bar
4 .	60x60x2mm
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	2 mm/min
8 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
STATEX® 18	ITW FORMEX	PP, Unspecified	STATEX®
Nycal™ 1850R13	Technical Polymers, LLC	Nylon 6	Nycal™
APEX® 85-J438D-8LG	Teknor Apex Company	PVC, Flexible	APEX®
Hostaform® C 9021 AW XAP² ™ LS	Celanese Corporation	Acetal (POM) Copolymer	Hostaform®
ULTEM™ 1285 resin	SABIC Innovative Plastics	PEI	ULTEM™