Generic EBA
| Category: | EBA , Ethylene Butyl Acrylate Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QlArRn_Generic-EBA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic EBA This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.922 - 0.950 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.45 - 44 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 0.20 - 4.6 | g/10 min | ISO 1133 |
| n-Butyl Acrylate Content | 3.0 - 17.2 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 45 - 46 | ASTM D2240 | |
| 23°C | 30 - 91 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture, 23°C | 12.0 - 14.3 | MPa | ASTM D638 |
| Fracture, 23°C | 7.70 - 14.3 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 600 - 860 | % | ASTM D638 |
| Fracture, 23°C | 590 - 830 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 99 - 200 | µm | |
| Tensile Stress | ISO 527-3 | ||
| Fracture, 23°C | 7.00 - 25.0 | MPa | ISO 527-3 |
| 23°C | 22.0 - 25.1 | MPa | ISO 527-3 |
| Tensile Elongation (Break, 23°C) | 350 - 900 | % | ISO 527-3 |
| Dart Drop Impact (23°C) | 600 - 1500 | g | ISO 7765-1 |
| Elmendorf Tear Strength | 3.9 - 15 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 40.0 - 80.0 | °C | ASTM D1525 |
| -- | 40.0 - 80.3 | °C | ISO 306 |
| Melting Temperature | 65.0 - 107 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 10 - 45 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 200 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic EBAThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 20 FR GREY 96.7685 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| SURPASS® FPs117-D | NOVA Chemicals | LLDPE | SURPASS® |
| Adell Polyamide BJ-13 Impact Modified | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| Fainplast PVC GS 60/AS | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Electrafil® ABS CF10 | Techmer Engineered Solutions | ABS | Electrafil® |