LNP™ STAT-KON™ DE002ER compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ql6ldK_LNPSTATKONDE002ERcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DE002ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding. Also known as: LNP* STAT-KON* Compound DC-1002 EM MR Product reorder name: DE002ER |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.20 - 0.40 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.29 - 0.43 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.060 - 0.32 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.17 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.66 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6960 | MPa | ASTM D638 |
| -- | 6800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 101 | MPa | ASTM D638 |
| Fracture | 103 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.8 | % | ASTM D638 |
| Fracture | 3.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6140 | MPa | ASTM D790 |
| -- | 6960 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 166 | MPa | ASTM D790 |
| -- | 171 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 560 | J/m | ASTM D4812 |
| 23°C 3 | 40 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 19.9 | J | ASTM D3763 |
| -- | 4.25 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 144 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 141 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 142 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 2.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 5.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYCOA Polyamide 5000 HSL | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| Bayfit® SA513 (85 Index) | Covestro - PUR | PUR, Unspecified | Bayfit® |
| APEX® 3701-60NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina IVORY PVC COMPOUND 105902-35/ 1-Y-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucon® CP6052 | LG Chem Ltd. | PC+ABS | Lucon® |