ADENE NHFAG
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | A.D. Compound spa |
| Trademark: | ADENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QhhRFS_ADENE-NHFAG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADENE NHFAG is a Polypropylene Copolymer (PP Copolymer) material filled with 20% talc. It is available in Europe or North America. Primary attribute of ADENE NHFAG: Copolymer. Typical application of ADENE NHFAG: Consumer Goods |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Ash Content | 20 | % | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 22.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 9.0 | % | |
| Break | 65 | % | |
| Flexural Modulus | 1750 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 15 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DELPET™ 80NR-S | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| ECP 121/1014 | TBA Electro Conductive Products Ltd. | EVA | ECP |
| ISPLEN® PP 070 G2M | REPSOL | PP Homopolymer | ISPLEN® |
| Leona™ FG173 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Karina BLACK PVC COMPOUND 750-48/ 1-F-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |