Curv™ C100A
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Propex Fabrics |
| Trademark: | Curv™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QhIKTL_Curv-C100A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A new generation thermoplastic composite Curv™ is a novel material made from Polypropylene that combines ther versatility and recyclability of a 100% thermoplastic with the high performance of a fiber reinforced composite. High stiffness, high tensile strength and outstanding impact resistance at low density are the remarkable properties of these materials. Product: Polypropylene/Polypropylene Thermoformable Composite Sheet Dimensions: Thickness: 0.3 to 3.0 mm Available Width: up to 1360 mm Standard Length: Any lenght up to 3 meters, thinner sheets available on roll Color: standard - black, other colors subejct to minimum volume |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | DIN 53495 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1 | 3500 | MPa | ISO 178 |
| Compressive Stress 2 | 300 | MPa | ISO 604 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Energy 3(2100 µm) | 40.0 | J | ISO 6603-2 |
| Tensile Modulus | ISO 527-3 | ||
| MD | 4200 | MPa | |
| TD | 4200 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD | 120 | MPa | |
| TD | 120 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break | 20 | % | |
| TD : Break | 20 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -40°C | No Break | ISO 179 | |
| 20°C | 120 | kJ/m² | ISO 179/2B |
| 23°C | > 250 | kJ/m² | ISO 179/2 |
| Notched Izod Impact Strength | ISO 180/B | ||
| -40°C | 600 | kJ/m² | |
| 20°C | 400 | kJ/m² | |
| Tensile Impact Strength 4(20°C, 2.10 mm) | 1000 | kJ/m² | ISO 8256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 102 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 160 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 175 | °C | ISO 306/B |
| CLTE - Flow (20 to 80°C) | 6.8E-5 | cm/cm/°C | DIN 53752 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Fire Rating - Building Materials | B2 | DIN 4102 |
| Note Message | |
|---|---|
| 1 . | TD, flat wise |
| 2 . | flat wise |
| 3 . | 20°C, 52 J |
| 4 . | TD, 52 J |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600 GV 45 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Geon™ Vinyl Flexible B9000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| GPPC PS-350S | GPPC Chemical Co., Ltd. | PS (HIPS) | GPPC |
| Hostacom G4 R01 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| VALOX™ DR48 resin | SABIC Innovative Plastics | PBT | VALOX™ |