ANSABLEND A15 000 0000 T65 V0
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Daloga srl |
| Trademark: | ANSABLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QhCb3U_ANSABLEND-A15-000-0000-T65-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ANSABLEND A15 000 0000 T65 V0 is a Polycarbonate + ABS (PC+ABS) material. It is available in Europe for injection molding. Important attributes of ANSABLEND A15 000 0000 T65 V0 are:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 12 to 27 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow | 0.50 to 0.70 | % | |
| Flow | 0.50 to 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 60.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 150 to 250 | J/m | ASTM D256 |
| -- | 14 to 28 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | > 100 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index 3 | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 48 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8852 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Sup-tech P280 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| YUNGSOX® PP 5003 | Formosa Polypropylene | PP Random Copolymer | YUNGSOX® PP |
| Braskem PP DR152.02 | Braskem Europe GmbH | PP Random Copolymer | Braskem PP |
| Polygen SG8C | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |