Vandar® 2100
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Vandar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QgIFgf_Vandar-2100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vandar 2100 is a polyester alloy designed to offer maximum impact strength at room and low temperatures. This unfilled compound is characterized by outstanding chemical resistance, dimensional stability, paintability, and toughness. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 5.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.8 | % | ASTM D955 |
| Vertical flow direction | 1.7 - 2.2 | % | ISO 294-4 |
| Flow direction | 1.7 - 2.2 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 109 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, 23°C | 43.4 | MPa | ASTM D638 |
| Yield | 40.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 28.0 | MPa | ISO 527-2/1A/50 |
| 50% strain | 26.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain | |||
| Yield | 4.0 | % | ISO 527-2/1A/50 |
| Fracture, 23°C | 150 | % | ASTM D638 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 1650 | MPa | ISO 178 |
| Flexural Stress (23°C) | 53.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 16 | kJ/m² | ISO 179/1eA |
| 23°C | 80 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C) | 70 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 104 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 48.9 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 50.0 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 60.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 137 | °C | ISO 306/B50 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3, ASTM D3418 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 24 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.00 | IEC 60250 | |
| 1 MHz | 3.60 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 7.0E-3 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 96.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIMMA® FT6130 | Samyang Corporation | Acrylic (PMMA) | TRIMMA® |
| Axiall PVC 19451 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| DESLON™ 6 DSC101M6 | DESCO Co., Ltd. | Nylon 6 | DESLON™ 6 |
| Hypro® PPC-GF25 NATURAL | Entec Polymers | PP Impact Copolymer | Hypro® |
| TOTAL Polyethylene TPSeal® M 3671 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |