Kelon® B FR H2 CEG/500-V0CT3
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Kelon® B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qg9MZg_Kelon-B-FR-H2-CEG-500-V0CT3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Heat stabilised. Mineral filler / Glass fibres. UL94 V-0 classified, halogens and red phosphorus free. Product UL certified. Low thermal expansion coefficient. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.50 to 0.65 | % | |
| Flow | 0.25 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| 23°C | 10500 | MPa | |
| 60°C | 6500 | MPa | |
| 90°C | 4700 | MPa | |
| 120°C | 3500 | MPa | |
| 150°C | 2800 | MPa | |
| Tensile Stress | ISO 527-2 | ||
| Break, 23°C | 85.0 | MPa | |
| Break, 60°C | 65.0 | MPa | |
| Break, 90°C | 55.0 | MPa | |
| Break, 120°C | 45.0 | MPa | |
| Break, 150°C | 35.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Break, 23°C | 1.5 | % | |
| Break, 60°C | 1.8 | % | |
| Break, 90°C | 2.0 | % | |
| Break, 120°C | 2.5 | % | |
| Break, 150°C | 2.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.5 | kJ/m² | |
| 23°C | 3.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 15 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 135 | °C | |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.5E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.90 | W/m/K | ASTM E1952-01 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-1 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature (1.00 mm) | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 42 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SureSpec PET-80 | Genesis Polymers | PET | SureSpec |
| NORYL™ SE1GFN1 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| EVALENE® PP PRJ1501 | JG Summit Petrochemical Corporation | PP Random Copolymer | EVALENE® PP |
| ExxonMobil™ LDPE LD 124.MS | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| LNP™ LUBRICOMP™ DBL34 compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |