VENYL SE032 - 8428
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qg6Xiu_VENYL-SE032---8428.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SE032 - 8428 is a high impact resistance reinforced polyamide 6 with detergent additives intended for Injection moulding. APPLICATIONS VENYL SE032 - 8428 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL SE032 - 8428 is available in natural (VENYL SE032) and other colours can be provided on request. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.10 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.0 to 2.0 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.7 to 2.9 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1550 | 650 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 45.0 | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 70 | 240 | % | ISO 527-2 |
| Flexural Modulus | 1300 | 600 | MPa | ISO 178 |
| Flexural Stress | 50.0 | 35.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 30 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | -- | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 155 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 235 to 240 | °C | |
| Front Temperature | 235 to 240 | °C | |
| Nozzle Temperature | 220 to 265 | °C | |
| Mold Temperature | 45.0 to 65.0 | °C | |
| Injection Pressure | 70.0 to 90.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 to 60.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP220R | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Witcom PP 2007/117 | Witcom Engineering Plastics B.V. | PP, Unspecified | Witcom PP |
| Daelim Po1y® TR-480SK | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| FERREX® GPP30CC38UL GRAY | Ferro Corporation | PP Homopolymer | FERREX® |
| Sarlink® TPE RV-2250D BLK 111 | Teknor Apex Company | TPE | Sarlink® TPE |