TOTAL Polystyrene 3341
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qg3zKb_TOTAL-Polystyrene-3341.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polystyrene Impact 3341 is a high ductility polystyrene for extrusion application. It offers good mechanical and thermal properties, that leads to manufacturing of thermoformed articles with good rigidity and toughness. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Apparent Density | 0.60 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Spiral Flow 1 | 44.0 | cm | ASTM D3123 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr | 0.070 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Grade R, 23°C, Injection Molding | 99 | ASTM D785 | |
| R scale, 23°C | 99 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, Injection Molded) | 32.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C, Injection Molded) | 45 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C, Injection Molded) | 2300 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, injection molding | 100 | J/m | ASTM D256 |
| 23°C, injection molding | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ISO 306/A50, ASTM D1525 2 |
| CLTE - Flow | 9.1E-5 | cm/cm/°C | ASTM D696 |
| Heat Distortion | |||
| -- | 80 | °C | ISO 75-2 |
| -- | 80 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Dielectric Strength | 150 | kV/mm | ASTM D149 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 - 180 | °C | |
| Cylinder Zone 2 Temp. | 170 - 210 | °C | |
| Cylinder Zone 3 Temp. | 190 - 230 | °C | |
| Cylinder Zone 4 Temp. | 200 - 240 | °C |
| Extrusion instructions |
|---|
| Nozzle: 210-250°C |
| Note Message | |
|---|---|
| 1 . | Mold temperature: 220°C |
| 2 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 65.NA | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| PRE-ELEC® PP 1384 | Premix Oy | TPO | PRE-ELEC® |
| Hostacom M2 N01 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Lupos® GP2300 | LG Chem Ltd. | ABS | Lupos® |
| Sylvin 9067-65 Black 284 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |