Celanex® 1632Z
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QfbGeq_Celanex-1632Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 1632Z is a general purpose, 15% fiberglass reinforced polybutylene terephthalate with a good balance of mechanical properties and processability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow | 0.30 - 0.70 | % | ASTM D955 |
| Flow direction | 0.30 - 0.50 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5200 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 93.1 | MPa | ASTM D638 |
| Fracture | 95.0 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 5.5 | % | ASTM D638 |
| Fracture | 5.4 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 5400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 155 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.4 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 5.3 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 217 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 213 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 192 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 189 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 60.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3, ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 3 | 18 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.40 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-3 | ASTM D150 | |
| Arc Resistance | 125 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F320 (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Auracell® H | Rotuba Extruders, Inc. | CA | Auracell® |
| DOWLEX™ 2645.01G | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Elvaloy® AC 34035 | DuPont Packaging & Industrial Polymers | EBA | Elvaloy® |
| Karina IVORY PVC COMP. 806-35/ 2-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |