Novalloy-B B5504
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Novalloy-B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QfPzLl_Novalloy-B-B5504.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Novalloy-B B5504 is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) product filled with 20% glass fiber. It can be processed by coating or injection molding and is available in North America. Applications of Novalloy-B B5504 include electrical/electronic applications, business/office goods, coating applications and housings. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.25 to 0.45 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 97.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 6470 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 142 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 200 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 125 | °C | |
| CLTE - Flow | 6.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (100 Hz) | 3.60 | ASTM D150 | |
| Dissipation Factor (100 Hz) | 3.0E-3 | ASTM D150 | |
| Arc Resistance (3.18 mm) | 71.0 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) (3.18 mm) | 375 | V | UL 746 |
| High Amp Arc Ignition (HAI) (1.59 mm) | 39.0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (1.59 mm) | 183 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) (1.59 mm) | 43 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | V-0 | ||
| 2.90 mm, ALL | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 121 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Processing (Melt) Temp | 241 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 0.483 to 1.45 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime 5490 | Prime PVC® | PVC, Rigid | Prime |
| SHIN-A SE-165 | SHIN-A T&C | Epoxy | SHIN-A |
| Estane® 58215 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Huafon JF-W-BK3060 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| LEXAN™ 3412R resin | SABIC Innovative Plastics | PC | LEXAN™ |