TRIBOCOMP® A-3 TS0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QecGBB_TRIBOCOMP-A-3-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® A-3 TS0 is a Polyamide 66 (Nylon 66) product. It is available in Europe. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.50 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 10500 | 7900 | MPa | |
| 90°C | 7100 | -- | MPa | |
| 120°C | 5500 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 205 | 160 | MPa | |
| Yield, 90°C | 135 | -- | MPa | |
| Yield, 120°C | 105 | -- | MPa | |
| Tensile Strain (Break, 23°C) | 3.0 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8300 | 6200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 280 | 200 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | |||
| vs. Itself - Dynamic | 0.23 | -- | ||
| vs. Itself - Static | 0.18 | -- | ||
| Wear Factor | 11 | -- | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 65 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 253 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.9E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.29 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | ASTM D257 |
| Electric Strength | 35 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 270 to 300 | °C | |
| Cylinder Zone 2 Temp. | 270 to 300 | °C | |
| Cylinder Zone 3 Temp. | 285 to 300 | °C | |
| Cylinder Zone 4 Temp. | 285 to 310 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SEP-600X40 | SHIN-A T&C | Phenolic | SHIN-A |
| YUPLENE® BH3720 | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| BESTPOLUX PCAHC/02 | Triesa Plastics | PC+ABS | BESTPOLUX |
| ELASTOSIL® AUX MOULD RELEASE A | Wacker Chemie AG | Silicone | ELASTOSIL® AUX |
| Karina IVORY PVC COMPOUND 751-35/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |