LubriOne™ PC-20CF/15T BK012
| Category: | PC , Polycarbonate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QeT9uv_LubriOne-PC-20CF-15T-BK012.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTFE lubricated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 120 | MPa | ASTM D638 |
| Flexural Modulus 2 | 11000 | MPa | ASTM D790 |
| Flexural Strength 3 | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 140 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 - 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 290 - 310 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Mold Temperature | 90.0 - 110 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SER-2001 | SHIN-A T&C | Epoxy | SHIN-A |
| TES J-70/30 BK8037 | Techmer Engineered Solutions | Nylon 66+PP | TES |
| ExxonMobil™ LLDPE LL 8450 Series | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Hifax TYC 337P 4 C13098 | LyondellBasell Industries | PP Copolymer | Hifax |
| LUVOCOM® 20-0951 VP | LEHVOSS Group | PPA | LUVOCOM® |