PTS PPE-LXS314-30
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Technology and Services, LLC |
| Trademark: | PTS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qe2SDF_PTS-PPE-LXS314-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTS PPE-LXS314-30 is a Polyphenylene Ether + PS (PPE+PS) product filled with 30% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Industrial Applications. Primary characteristic: impact resistant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.35 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 110 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus 4 | 5500 | MPa | ASTM D790 |
| Flexural Strength 5 | 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) | 14.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 135 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | solid |
| 2 . | Type I |
| 3 . | Type I |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon X1000-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| Chemlon® 257 H | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| ExxonMobil™ PP9122 | ExxonMobil Chemical | PP Random Copolymer | ExxonMobil™ |
| FHR Polypropylene P9R2M-062 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| DURANEX® 551HS | Polyplastics Co., Ltd. | PBT | DURANEX® |