REPOL® B300MN
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qdv2Om_REPOL-B300MN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
REPOL Polypropylene B300MN is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific catalyst system. Repol B300MN is high crystalline Impact Copolymer grade recommended for use in Injection Moulding processes. The grade contains nucleating agent. It is an ideal material for making automobile parts where high flow with very high stiffness is required. The grade is also suitable as a compounding base for automotive and appliance sectors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, Injection Molded) | 5.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(Injection Molded) | 1650 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 70.0 | J/m | ASTM D256 |
| Notched Izod Impact (23°C, Injection Molded) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Injection Molded) | 115 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T- 27 MT 30 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| UmaPET HQO/HQI | Ester Industries Ltd. | PET | UmaPET |
| apinat® DP2125 | API SpA | Biodeg Polymers | apinat® |
| LNP™ LUBRICOMP™ GL003XXP compound | SABIC Innovative Plastics Europe | PSU | LNP™ LUBRICOMP™ |
| TECHNYL® C 52G3 MZ25 GREY R7035 | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |