Lucon® PS6080EX
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QdWLUX_Lucon-PS6080EX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucon®PS-6080EX is an acrylonitrile butadiene styrene (ABS) material, which contains carbon nano-filler. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Lucon®The main features of the PS-6080EX are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.95 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 73.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | < 5.0 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 12900 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 127 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 20 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 250 | °C | ASTM D648 |
| Peak Melting Temperature | 280 | °C | ASTM D3418 |
| Thermal Conductivity 5 | 1.7 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+18 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| 2.50 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 280 - 310 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 320 - 325 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 | °C | |
| Mold Temperature | 130 - 150 | °C | |
| Back Pressure | 0.981 - 3.92 | MPa | |
| Screw Speed | 40 - 60 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.01% |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 1.0 mm/min |
| 5 . | Laser Flash Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROFIL™ PPC3GF03-BK | Pier One Polymers, Inc. | PP Copolymer | PROFIL™ |
| CALP WW175 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| China PPS hFR42 | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| Geon™ Vinyl Rigid Extrusion 87345 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| ESPOLEX WT502 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |