Kelon® B H CETG/300
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Kelon® B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QcYuxf_Kelon-B-H-CETG-300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 6 (PA 6). Heat stabilised. Mineral filler / Glass fibres. Product UL certified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.45 to 0.70 | % | |
| Flow : 2.00 mm | 0.35 to 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 8600 | MPa | |
| 60°C | 6300 | MPa | |
| 90°C | 3000 | MPa | |
| 120°C | 2200 | MPa | |
| 150°C | 1700 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 80.0 | MPa | |
| Break, 60°C | 60.0 | MPa | |
| Break, 90°C | 35.0 | MPa | |
| Break, 120°C | 30.0 | MPa | |
| Break, 150°C | 25.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.5 | % | |
| Break, 60°C | 3.2 | % | |
| Break, 90°C | 7.0 | % | |
| Break, 120°C | 15 | % | |
| Break, 150°C | 25 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 40 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | °C | |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cheng Yu SW15 | Cheng Yu Plastic Company Limited | Acetal (POM) Copolymer | Cheng Yu |
| LEXAN™ HFD1433 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Jiangsu Sinarise PX851X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Karina GRAY PVC COMPOUND -E 75850-18/283-CY-AC-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OmniLon™ PA6/6 U IM20 HS BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |