RTP 2800B-40A
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QbyM5l_RTP-2800B-40A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. 40 Shore A |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.9 - 2.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 45 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 2.76 | MPa | ASTM D412 |
| Tensile Elongation 2(Break) | 500 | % | ASTM D412 |
| Tear Strength 3 | 14.9 | kN/m | ASTM D624 |
| Additional Information |
|---|
| Moisture Content: 0.08% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | > 4.0 | hr | |
| Processing (Melt) Temp | 193 - 210 | °C | |
| Mold Temperature | 10.0 - 79.4 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GF 30 GID | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Sindustris PP HF5158 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| TABOREN PC 41 G 10 | SILON s.ro | PP Copolymer | TABOREN |
| Generic PC - Proprietary | Generic | PC | Generic |
| POLYfill PPC T8020 FC | Polykemi AB | PP Copolymer | POLYfill |