LNP™ LUBRICOMP™ LGL33 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QbOuY1_LNP-LUBRICOMP-LGL33-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* LGL33 is a compound based on Polyetheretherketone resin containing Graphite and PTFE. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-L-90086 Product reorder name: LGL33 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.47 | g/cm³ | |
| -- | 1.46 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.3 | % | |
| Across Flow : 24 hr | 1.5 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.030 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4310 | MPa | ASTM D638 |
| -- | 4290 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 65.0 | MPa | ASTM D638 |
| Break | 65.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 3.9 | % | ASTM D638 |
| Break | 3.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 4380 | MPa | ASTM D790 |
| -- 5 | 4250 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 116 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 119 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.36 | ||
| vs. Itself - Static | 0.39 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.550 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 46.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 44 | J/m | ASTM D256 |
| 23°C 7 | 4.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 360 | J/m | ASTM D4812 |
| 23°C 8 | 23 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.60 | J | ASTM D3763 |
| -- | 1.46 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 298 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 247 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 161 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 154 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 95N5156 | The Matrixx Group, Inc. | PC+ABS | Matrixx |
| Sasol Polymers PE HR477 | Sasol Polymers | LLDPE | Sasol Polymers PE |
| LTP ZW-3212 | Chengdu Letian Plastics Co., Ltd | Acetal (POM) Copolymer | LTP |
| Dutral® TX 1301 | Versalis S.p.A. | EPDM | Dutral® |
| StarClear® 1025-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarClear® |