Resilience™ LS11170E
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Resilience™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QazOXh_ResilienceLS11170E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Resilience™LS11170E is a rigid polyvinyl chloride product,. It can be processed by extrusion and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: lighting equipment. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 0 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 81 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8070 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 54.7 | MPa | ASTM D638 |
| Flexural Modulus | 7720 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 32 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 9.34 | J/cm | ASTM D4226 |
| 23°C 4 | 9.34 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 79.1 | °C | ASTM D648 |
| 0.45 MPa, annealed | 79.9 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 75.8 | °C | ASTM D648 |
| 1.8 MPa, annealed | 77.9 | °C | ASTM D648 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.3 mm, GY) | V-0 5VA | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Nylon 1015GNKF | UBE Industries, Ltd. | Nylon 6 | UBE Nylon |
| 3M™ Dyneon™ Fluoroplastic FEP 6322HTZ | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| alphalon™ 27 C | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| ATPioneers Acrylic ACN 102 | Asia Technology Pioneers Ltd | Acrylic, Unspecified | ATPioneers Acrylic |
| Sylvin 916VO Yellow 4152 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |