LNP™ STAT-KON™ Cycoloy_JK800 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qanf58_LNP-STAT-KON-Cycoloy-JK800-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON CYCOLOY_JK800 compound is an 8% carbon fiber reinforcedPC+ABS, electrostatic dissipative ECO conforming FR. Good hydrolytic stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.10 to 0.20 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7580 | MPa | ASTM D638 |
| -- | 7500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 96.5 | MPa | ASTM D638 |
| Yield | 95.0 | MPa | ISO 527-2/5 |
| Break 3 | 96.5 | MPa | ASTM D638 |
| Break | 95.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.9 | % | ASTM D638 |
| Yield | 1.9 | % | ISO 527-2/5 |
| Break 5 | 1.9 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 6210 | MPa | ASTM D790 |
| -- 7 | 6380 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 145 | MPa | ISO 178 |
| Break, 50.0 mm Span 8 | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 9 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 350 | J/m | ASTM D4812 |
| 23°C 10 | 21 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 82.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 97.2 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 92.2 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 94.4 | °C | |
| Vicat Softening Temperature | |||
| -- | 111 | °C | ASTM D1525 11 |
| -- | 101 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 7.4E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Static Decay 12 | 10 | msec | FTMS 101B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.991 mm | V-0 | ||
| 1.50 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 210 to 254 | °C | |
| Middle Temperature | 216 to 260 | °C | |
| Front Temperature | 227 to 274 | °C | |
| Nozzle Temperature | 232 to 274 | °C | |
| Processing (Melt) Temp | 232 to 274 | °C | |
| Mold Temperature | 48.9 to 71.1 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | Rate B (120°C/h), Loading 2 (50 N) |
| 12 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Roscom PVC 601VO-75/80 | Roscom, Inc. | PVC, Flexible | Roscom PVC |
| Sinpolene MFP14ZA3 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| TEKAMID™ TB120G15 | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| TERRAMAC TE-7000 | UNITIKA Plastics Division | PLA | TERRAMAC |
| ENVIROPLAS® ENV00-NC700 | ENVIROPLAS®, Inc. | ABS | ENVIROPLAS® |