KOPLA PA66 KDX1067
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QaiHHA_KOPLA-PA66-KDX1067.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PA66 KDX1067 is a Polyamide 66 (Nylon 66) material filled with glass\mineral. It is available in Asia Pacific. Important attributes of KOPLA PA66 KDX1067 are:
Typical application of KOPLA PA66 KDX1067: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 to 1.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 73.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3730 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 98.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 250 | °C | |
| 1.8 MPa, Unannealed | 230 | °C | |
| Melting Temperature | 260 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 26 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® B BR0M6 | Nanjing Julong Engineering Plastics Co., LTD | Nylon 6 | Wondel® B |
| Ultramid® B3M8 (8260) | BASF Corporation | Nylon 6 | Ultramid® |
| AKROMID® A3 GF 30 1 L natural (4715) | AKRO-PLASTIC GmbH | Nylon 66+PP | AKROMID® |
| Petlon R-Prime C3-G30-00-BK | Petlon Polymers Ltd | Nylon 66/6 | Petlon R-Prime |
| Plexiglas® V825NA | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |