AKROMID® B3 GFM 10/20 1 black 950089 (2017)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qag6lv_AKROMID-B3-GFM-10-20-1-black-950089-2017-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GFM 10/20 1 black 950089 (2017) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability Applications areas are optical engine covers in the automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4000 | MPa | ISO 178 |
| Flexural Stress 2 | 170 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 5.5 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 55.0 | °C | ISO 75-2/C |
| Melting Temperature 4 | 222 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Fluorosint® HPV | Quadrant Engineering Plastic Products | PTFE | Quadrant EPP |
| TAISOX 9000 | Formosa Plastics Corporation | HDPE | TAISOX |
| Baoding 68T95 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Geon™ Vinyl Flexible B5D00 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| EMOPLEN® A 440 T35 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |