VAMPAMID 66 3530 V0 P
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QaP5KH_VAMPAMID-66-3530-V0-P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL 94 V0 at 0,8 mm, 35 % glass fiber, red phosphorus, good mechanical properties, GWFI 960/1-2, GWIT 775/1-2. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | |
| Across Flow | 0.80 | % | |
| Water Absorption (Saturation) | 0.80 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 155 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 8.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 50 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 245 | °C | ASTM D648A |
| Vicat Softening Temperature | 245 | °C | ASTM D1525 1 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 to 2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 to 2.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 275 | °C | |
| Mold Temperature | 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1324 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Beetafin® L9015 | BIP (Oldbury) Limited | PUR-Ester | Beetafin® |
| ENGAGE™ 8452 | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| HIVOREX 8100GX | Lotte Chemical Corporation | HDPE | HIVOREX |
| LNP™ STAT-KON™ DEL13EXC compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |