Order Products : sales@su-jiao.com
VENYL SG307 - 8139
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QaGORt_VENYL-SG307---8139.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SG307 - 8139 is a 30 % glass fibre reinforced polyamide 6 intended for Injection moulding. APPLICATIONS VENYL SG307 - 8139 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL SG307 - 8139 is available in both grey and natural (VENYL SG307) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 to 0.80 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (L-Scale) | 105 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8500 | 5000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 155 | 95.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 7500 | 4600 | MPa | ISO 178 |
| Flexural Stress | 250 | 175 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 12 | 18 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 40 | 50 | kJ/m² | ISO 179 |
| Notched Izod Impact | 70 | 100 | J/m | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Nozzle Temperature | 255 to 275 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Beetle® PBTS100T | Teknor Apex Company (Chem Polymer) | PBT | Beetle® |
| ExxonMobil™ HDPE HMA 018 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| IROCOAT® CA-271 | Huntsman Corporation | TPU, Unspecified | IROCOAT® |
| Lucky Enpla LGF3300 | Lucky Enpla Co LTD | PBT | Lucky Enpla |
| Sylvin 802-88 Yellow 433 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |