Kangxi® NHFRPA6-25GF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Wuxi Kangxi Plastics Technology Co.,Ltd. |
| Trademark: | Kangxi® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QZKGQm_KangxiNHFRPA625GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kangxi®NHFRPA6-25GF is a polyamide 6 (nylon 6) product, which contains a 25% glass fiber reinforced material. It can be processed by injection molding and is available in the Asia-Pacific region. Typical application areas are: electrical/electronic applications. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | 100 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 4 | 5000 | MPa | ASTM D790 |
| Flexural Strength 5 | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 210 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 180 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.6 mm | V-2 | UL 94 | |
| 3.2 mm | V-2 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weather Resistance - 24 hr (23°C) | 0.85 | % | ASTM D570 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95 | °C | |
| Drying Time | 6.0 | hr | |
| Rear Temperature | 220 - 250 | °C | |
| Middle Temperature | 220 - 250 | °C | |
| Front Temperature | 220 - 250 | °C | |
| Processing (Melt) Temp | 230 - 255 | °C | |
| Mold Temperature | 40 - 70 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 8300R | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| AMTOPP CH18 | Inteplast Group | PP, Unspecified | AMTOPP |
| Karina WHITE PVC COMPOUND -E 836-10/176-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| COSMOPLENE® AX191 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| ULTEM™ ATX3562R resin | SABIC Innovative Plastics | PEI+PCE | ULTEM™ |