AKROMID® B3 GF 60 4 RM-M black (5238)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QZHfN1_AKROMIDB3GF604RMMblack5238.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish. Applications are housings and other dimensional stable parts in the automotive and electronic industry demanding high resistance against CaCl2-solvents, as well as a very good surface. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.74 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.60 | -- | % | ISO 294-4 |
| Flow | 0.35 | -- | % | ISO 294-4 |
| Humidity Absorption - 62% RH (70°C) | 1.1 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 60 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 22500 | 17000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 225 | 175 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | 2.7 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 18 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 22 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 55 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 60 | 65 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, not annealed | 205 | -- | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 165 | -- | °C | ISO 75-2/C |
| Melting Temperature 1 | 225 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.8 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermoset Plastics UR-124 | Thermoset, Lord Chemical Products | PUR, Unspecified | Thermoset Plastics |
| VESTAMID® NRG 4101 yellow | Evonik Industries AG | Nylon 12 | VESTAMID® NRG |
| Bayflex® XGT-140 | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| Clyrell EC340R | LyondellBasell Industries | PP, Unspecified | Clyrell |
| Elastron® G G101.A83.N | Elastron USA, Inc. | SEBS | Elastron® G |