TRANSMARE® BIO M106
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® BIO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QZDyVC_TRANSMARE-BIO-M106.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 2600 | MPa | ISO 527-2/50 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00mm, injection molding | 49.0 | MPa | ISO 527-2/50 |
| Fracture, 4.00mm, injection molding | 16.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00mm, injection molding | 2.7 | % | ISO 527-2/50 |
| Fracture, 4.00mm, injection molding | 15 | % | ISO 527-2/50 |
| Flexural Modulus 1(Injection Molded) | 2300 | MPa | ISO 178 |
| Flexural Stress 2(Injection Molded) | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C, injection molding | 2.5 | kJ/m² | ISO 179/1A |
| -20°C, injection molding | 3.3 | kJ/m² | ISO 179/1A |
| 0°C, injection molding | 4.5 | kJ/m² | ISO 179/1A |
| 23°C, injection molding | 5.0 | kJ/m² | ISO 179/1A |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C, injection molding | 3.0 | kJ/m² | ISO 180/1A |
| -20°C, injection molding | 4.0 | kJ/m² | ISO 180/1A |
| 0°C, injection molding | 5.5 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 6.4 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 50.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 48.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 57.0 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 50.0 | °C | |
| Drying Time - Desiccant Dryer | 4.0 | hr | |
| Dew Point - Desiccant Dryer | -40.0 | °C | |
| Suggested Max Moisture | 0.30 | % | |
| Processing (Melt) Temp | 150 - 190 | °C |
| Injection instructions |
|---|
| Air Flow Rate: 120 m³/hr |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razalen® Q121 | Razin™ Engineering Plastics | PP Homopolymer | Razalen® |
| TRYCITE™ 8202 | The Dow Chemical Company | PS Alloy | TRYCITE™ |
| Cheng Yu A700UV | Cheng Yu Plastic Company Limited | ABS | Cheng Yu |
| Infino GP-3200G | SAMSUNG SDI CO., LTD. | ABS+PBT | Infino |
| Sylvin 29168-80 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |