Hostacom M2 T02
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QZ0Gof_Hostacom-M2-T02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom M2 T02 is a 20% mineral filled PP homopolymer with high flow, good stiffness and high heat resistance. It is not intended for medical, pharmaceutical or drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 6.0 | g/10 min | |
| 230°C/5.0 kg | 26 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 230°C/2.16 kg | 7.00 | cm³/10min | |
| 230°C/5.0 kg | 30.0 | cm³/10min | |
| Molding Shrinkage | 0.90 to 1.1 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 33.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus - Secant | 2900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (Area) (23°C) | 3.50 | kJ/m² | DIN 53453 |
| Impact Strength (23°C) | 25.0 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 74.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVAPOL® TF-Y822 Series | NOVA Chemicals | LLDPE | NOVAPOL® |
| ALFATER XL® A50I 4FC0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Keliren® CM366 | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| Kepital® TE-23S | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| Monprene® CP-19963 NAT (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |