Order Products : sales@su-jiao.com
ENFLEX EA3770A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | ENPLAST Americas, a Ravago Group Company |
| Trademark: | ENFLEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QYiFvD_ENFLEX-EA3770A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 70 Shore A TPE (Styrenic Block Copolymer based) available in black and natural for injection molding and extrusion applications. This grade offers soft/tactile feel and adhesion (overmolding or co-extrusion) to ABS, PC and HIPS/PS. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.988 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 10 seconds, extruded | 67 | ASTM D2240 | |
| Shore A, 10 seconds, injection molding | 70 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 1.90 | MPa | ASTM D412 |
| Tensile Strength (Break) | 6.00 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 550 | % | ASTM D412 |
| Tear Strength | 33.3 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 25 | % | ASTM D395B |
| 70°C, 22 hr | 65 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -40.0 | °C | ASTM D746 |
| Dynamic Service Temperature | 90 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 54.4 - 71.1 | °C | |
| Rear Temperature | 149 - 171 | °C | |
| Middle Temperature | 171 - 191 | °C | |
| Front Temperature | 199 - 221 | °C | |
| Nozzle Temperature | 199 - 221 | °C | |
| Processing (Melt) Temp | 191 - 210 | °C | |
| Mold Temperature | 10.0 - 48.9 | °C | |
| Injection Pressure | 5.17 - 8.96 | MPa | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 200 | rpm | |
| Clamp Tonnage | 3.4 - 4.8 | kN/cm² | |
| Cushion | 5.08 - 12.7 | mm |
| Injection instructions |
|---|
| Holding Time: 5 to 7 Sec. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 54.4 - 71.1 | °C | |
| Hopper Temperature | 149 - 171 | °C | |
| Cylinder Zone 1 Temp. | 171 - 191 | °C | |
| Cylinder Zone 3 Temp. | 171 - 191 | °C | |
| Cylinder Zone 5 Temp. | 179 - 199 | °C | |
| Adapter Temperature | 179 - 210 | °C | |
| Melt Temperature | 191 - 221 | °C | |
| Die Temperature | 179 - 210 | °C |
| Extrusion instructions |
|---|
| Screw: L/D 20:1 or greater (L/D 24:1 preferred)Cooling Water: 60 - 85°F (15-30°C)Screw Speed: 100 - 200 rpmScreen Pack: 20/40/60 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-961U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| SUSTAPEEK MOD | Röchling Sustaplast SE & Co. KG | PEEK | SUSTAPEEK |
| DOW™ HDPE 82054P | The Dow Chemical Company | HDPE | DOW™ HDPE |
| PENTAMID AHT MC30 H ungefärbt | PENTAC Polymer GmbH | Nylon 46 | PENTAMID AHT |
| LNP™ LUBRICOMP™ EL003 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |