Badadur® PBT8 GF30 FR HF
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Bada AG |
| Trademark: | Badadur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QYOC60_Badadur-PBT8-GF30-FR-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity, 30 % GF reinforced, non halogenated flame retardent injection moulding grade with very good mechanical properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.32 | % | |
| Equilibrium, 23°C, 50% RH | 0.13 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 7500 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break, 23°C) | 100 | MPa | ISO 527-2/5 |
| Tensile Strain 3(Break, 23°C) | 2.8 | % | ISO 527-2/5 |
| Flexural Stress 4(23°C) | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5 | |||
| -30°C | 7.0 | kJ/m² | ISO 179 |
| 23°C | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 6 | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Notched Izod Impact Strength 7(23°C) | 6.0 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 9 | 223 | °C | ISO 3146 |
| CLTE 10 | |||
| Flow | 4.2E-5 | cm/cm/°C | DIN 53752 |
| Transverse | 1.0E-4 | cm/cm/°C | DIN 53754 |
| Maximum Service Temperature | IEC 216 | ||
| 20000 hrs | 135 | °C | |
| some hours | 170 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 11 | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity 12 | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength 13 | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity 14(1 MHz) | 3.60 | IEC 60250 | |
| Dissipation Factor 15(1 MHz) | 0.017 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 16(1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 245 to 265 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 80x10x4 mm |
| 8 . | 110x10x4 mm |
| 9 . | 10 K/min, Compound moulding |
| 10 . | >=10x10x4 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 80x80x1 mm |
| 15 . | 80x80x1 mm |
| 16 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene 3241 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Vatpol 401 | Vatan Plastik San. Tic. AS | PP, Unspecified | Vatpol |
| Fluon® PFA P-66PT | Asahi Glass Co., Ltd. | PFA | Fluon® |
| Eltex® HD5211GA-B | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |
| Estane® 2103-85AE TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |