LNP™ LUBRICOMP™ DL004 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QYF3Np_LNPLUBRICOMPDL004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DL004 is a compound based on Polycarbonate resin containing PTFE. Added features include Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound DL-4040 Product reorder name: DL004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 47.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 5.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Flexural Stress | 77.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.25 | ASTM D3702 Modified | |
| With Self-Static | 0.21 | ASTM D3702 Modified | |
| Wear Factor - Washer | 31.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 17 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, unannealed, 64.0mm span | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 127 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 7.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 7.9E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 304 - 316 | °C | |
| Front Temperature | 310 - 321 | °C | |
| Processing (Melt) Temp | 299 - 316 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6911 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Tenac™ 4013A | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Ultrason® S 6010 | BASF Corporation | PSU | Ultrason® S |
| ALCOM® POM 770/1.1 CF20 | ALBIS PLASTIC GmbH | Acetal (POM) Copolymer | ALCOM® POM |
| Ferro PP TPP40AF23TN | Ferro Corporation | PP Homopolymer | Ferro PP |