Order Products : sales@su-jiao.com
LNP™ THERMOCOMP™ DF006P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QWg0iB_LNP-THERMOCOMP-DF006P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* DF006P is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Exceptional Processing. Also known as: LNP* THERMOCOMP* Compound DF-1006 EP Product reorder name: DF006P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.15 | % | ASTM D955 |
| Across Flow : 24 hr | 0.67 | % | ASTM D955 |
| Across Flow : 24 hr | 0.51 | % | ISO 294-4 |
| Flow : 24 hr | 0.090 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10500 | MPa | ASTM D638 |
| -- | 10000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 125 | MPa | ASTM D638 |
| Yield | 125 | MPa | ISO 527-2/5 |
| Break 3 | 125 | MPa | ASTM D638 |
| Break | 125 | MPa | ISO 527-2/5 |
| Tensile Elongation 4 | ASTM D638 | ||
| Yield | 2.4 | % | |
| Break | 2.4 | % | |
| Flexural Modulus 5(50.0 mm Span) | 8730 | MPa | ASTM D790 |
| Flexural Strength 6 | ASTM D790 | ||
| Yield, 50.0 mm Span | 165 | MPa | |
| Break, 50.0 mm Span | 165 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 7 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 770 | J/m | ASTM D4812 |
| 23°C 8 | 48 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.0 | J | ASTM D3763 |
| -- | 2.18 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 134 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 131 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 134 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, Testing by SABIC | V-2 | ||
| 3.00 mm, Testing by SABIC | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP229R | LyondellBasell Industries | Polyolefin, Unspecified | Moplen |
| Keltan® 6950 | LANXESS Buna GmbH | EPDM | Keltan® |
| HI-ZEX™ 530B | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| Karina BROWN COLOR CONCENTRATE 36/234-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucel® N127LD | LG Chem Ltd. | Acetal (POM) Copolymer | Lucel® |