ASTALON™ E1600MU
| Category: | PC , Polycarbonate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QWXzC7_ASTALON-E1600MU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTALON™ E1600MU is an ultra high viscosity, branched polycarbonate grade specifically designed for multi-wall sheet and profile extrusion applications. E1600MU offers an excellent balance of transparency, toughness, UV stability, flame retardancy and processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 140 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 800 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 85.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 150 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 135 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 125 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Cylinder Zone 1 Temp. | 240 to 250 | °C | |
| Cylinder Zone 2 Temp. | 245 to 270 | °C | |
| Cylinder Zone 3 Temp. | 250 to 270 | °C | |
| Cylinder Zone 4 Temp. | 260 to 275 | °C | |
| Cylinder Zone 5 Temp. | 250 to 270 | °C | |
| Melt Temperature | 260 to 280 | °C | |
| Die Temperature | 240 to 270 | °C | |
| Take-Off Roll | 80.0 to 90.0 | °C | |
| Back Pressure | 10.0 to 25.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 20 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 A FR | RTP Company | Nylon 6 | RTP |
| RTP 2182 | RTP Company | PEI | RTP |
| Trivin™ 212 | Vi-Chem Corporation | PVC, Unspecified | Trivin™ |
| LEXAN™ LGK3020 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LNP™ LUBRICOMP™ XFL21R compound | SABIC Innovative Plastics | Nylon, Unspecified | LNP™ LUBRICOMP™ |